HIGH-DENSITY POLYETHYLENE RESIN COMPOSITION HAVING HIGH ENVIRONMENTAL STRESS CRACK RESISTANCE
HIGH-DENSITY POLYETHYLENE RESIN COMPOSITION HAVING HIGH ENVIRONMENTAL STRESS CRACK RESISTANCE
展开▼
机译:具有高环境应力抗裂性的高密度聚乙烯树脂组合物
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to a high-density polyethylene resin composition having high environmental stress cracking resistance, comprising 60 to 70% by weight of a polyethylene resin and 30 to 40% by weight of an ethylene-alpha-olefin copolymer resin, wherein the polyethylene resin is melt flow The index is 100 to 300 g / 10 min (measured at 190 ° C., a load of 2.16 kg), the density is 0.950 to 0.980 / ㎤, and the ethylene-alpha-olefin copolymer resin has a melt flow index of 0.01 to 2 g / 10 min ( 190 ° C., and a load of 2.16 kg), and a density of 0.930 to 0.960 g/cm 3 , as a melt-mixed mixture of the polyethylene resin and the ethylene-alpha-olefin copolymer resin, and a melt flow index (MFI) of 5 to 10 g/10 min (measured under the conditions of 190° C. and a load of 2.16 kg) and a density of 0.950 to 0.970 g/cm 3 is provided.
展开▼
机译:本发明涉及具有高环境应力裂化抗性的高密度聚乙烯树脂组合物,其包含60至70重量%的聚乙烯树脂和30至40重量%的乙烯-α-烯烃共聚物树脂,其中聚乙烯树脂熔融流动折射率为100至300g / 10min(在190℃下测量,负荷为2.16kg),密度为0.950至0.980 /‰,乙烯-α-烯烃共聚物树脂具有熔体流量指数为0.01至2g / 10 min(190℃,载荷为2.16kg),密度为0.930至0.960g / cm 3,作为聚乙烯树脂和乙烯的熔融混合混合物 - α-烯烃共聚物树脂和5至10g / 10分钟的熔体流动指数(MFI)(在190℃的条件下测量,载荷为2.16千克),密度为0.950至0.970g / cm 3提供。
展开▼