Method For Improving Performance Of Sintered Ndfeb Magnets

摘要

The present disclosure relates generally to a method for improving the performance of sintered NdFeB magnet. A method of preparing a sintered NdFeB magnet therefore comprises the steps of: a) preparing alloy flakes from a raw material of the NdFeB magnet by a strip casting process; and b) preparing a coarse alloy powder from the alloy flakes by a hydrogen decrepitation process, the hydrogen decrepitation process including treatment of the alloy flakes under a hydrogen pressure of 0.10 MPa to 0.25 MPa for a duration of 1 to 3.5 hours, then degassing the hydrogen at a predetermined temperature between 300° C. to 400° C. for a duration time of 0.5 to 5 hours, and then mixing the resulting coarse alloy powder with a lubricant.