LOW-COST AND HIGH-FORMABILITY 1180 MPA GRADE COLD-ROLLED ANNEALED DUAL-PHASE STEEL PLATE AND MANUFACTURING METHOD THEREOF

摘要

A low-cost and high-formability 1180 MPa grade cold-rolled annealed dual-phase steel plate and a manufacturing method thereof are provided. The dual-phase steel plate has the following chemical composition by mass percentages: C: 0.1%-0.125%, Si: 0.4%-0.8%, Mn: 2.6%-2.9%, Al: 0.01%-0.05%, Nb: 0.01%-0.03%, and Ti: 0.01%-0.03%, the remainder being Fe and unavoidable impurities. By reasonable design of alloy elements and manufacturing processes, the dual-phase steel plate of the invention achieves a strength of 1180 MPa grade at a low cost, obtains a fine and uniform martensite-ferrite dual-phase structure that ensures excellent elongation rate and cold bending performance, and has good formability. The dual-phase steel plate has a yield strength of more than 850 MPa, a tensile strength of more than 1180 MPa, an elongation rate of 8% or more, and a parameter (R/t), characterizing the 90-degree cold bending performance, of 2.5 or less.