Brazing paste and method of brazing using brazing paste
Brazing paste and method of brazing using brazing paste
展开▼
机译:钎焊膏及使用该钎焊膏的钎焊方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
871,813. Brazing. MARTIN CO. Dec. 1, 1958, No. 38627/58. Class 83 (4). A brazing paste for joining aluminium or aluminium base alloys containing at least 70% aluminium comprises approximately 1 part by weight of a metal fluoride, from approximately 4-12 parts by weight of an aluminium-silicon alloy and water. In an example a paste is prepared using 4-12, preferably 7-8 parts by weight of powdered aluminium-silicon alloy, 1 part by weight powdered aluminium fluoride and 3¢ parts by weight water. The alloy may contain 7-12 parts aluminium and 1 part silicon, e.g. 88% aluminium and 12% silicon. The paste, which is brushed on to the joint, may be used in furnace or flux dip brazing and one of the parts to be joined may be an aluminiummagnesium-copper bearing alloy.
展开▼
机译:871,813。钎焊。 MARTIN CO.1958年12月1日,编号38627/58。 83级(4)。用于接合铝或包含至少70%的铝的铝基合金的钎焊膏包括大约1重量份的金属氟化物,大约4-12重量份的铝-硅合金和水。在一个实例中,使用4-12重量份,优选7-8重量份的铝硅粉末粉末,1重量份的氟化铝粉末和3¢重量份的水制备糊剂。该合金可以包含7-12份铝和1份硅,例如88%的铝和12%的硅。涂在接头上的糊剂可用于熔炉或熔剂浸渍钎焊中,要连接的零件之一可以是铝镁铜合金。
展开▼