LINING OF REGENERATORS OF GLASS FURNACES AND BURNER BLOCKS OF TUNNEL FURNACES
LINING OF REGENERATORS OF GLASS FURNACES AND BURNER BLOCKS OF TUNNEL FURNACES
展开▼
机译:隧道窑玻璃窑炉和燃烧器砌块的内衬
展开▼
页面导航
摘要
著录项
相似文献
摘要
1410205 Refractory bricks OSTERREICHISCH-AMERIKANISCHE MAGNESIT AG 11 Dec 1972 [22 Dec 1971] 57022/72 Heading C1A Bricks used for burner blocks of tunnel furnaces are made of magnesium aluminate containing at least 96% MgO and Al 2 O 3 , a CaO content of at most 0À50% and having a porosity of at most 15%, preferably below 10% and preferably below 0À30%. The bricks can be formed of magnesium aluminate produced in a spray reactor and sintered at a temp. of at least 1850‹ C. without a sintering aid or sintered at 1750‹ to 1800‹ C. together with 0À5 to 2À0% of TiO 2 based on the wt. of the aluminate, as a sintering aid, or of magnesium aluminate produced by fusing a mixture of MgO and Al 2 O 3 and comminuting the fused material.
展开▼
机译:1410205耐火砖OSTERREICHISCH-AMERIKANISCHE MAGNESIT AG 1972年12月11日[1971年12月22日]税号C1A用于隧道炉燃烧器砖的砖是由铝酸镁制成的,铝酸镁含量至少为96%MgO和Al 2 O 3,CaO含量为最多0-50%,孔隙率最多15%,优选低于10%,优选低于0-30%。砖可以由在喷雾反应器中产生并在一定温度下烧结的铝酸镁形成。至少在1850°C的温度下没有烧结助剂,或者在1750°至1800°C的温度下与重量百分比为0-5至2-0%的TiO 2一起烧结。通过烧结MgO和Al 2 O 3的混合物并粉碎熔融材料而生产的铝酸盐,作为烧结助剂或铝酸盐镁。
展开▼