In a continuous annealing process for rimmed steels having /=0.06% carbon content, the coiling temperature of said steel while in a strip form, hot and rolling is more than 630 DEG C to form massive carbides in said steel strip then after known coil reducing, is given a rapid cooling rate from a holding temperature during a continuous annealing stage of more than 50 DEG C/sec, subesequent shelf treating temperature of said traveling strip is within the range of 300 DEG C to 500 DEG C for at least 10 seconds, and then said strip is coiled after cooling to room temperature, consequently low yield point of less than about 23kg/mm2, and retarded aging property and good drawability are exhibited.
展开▼
机译:在碳含量≤0.06%的钢的连续退火工艺中,在带状,热轧和热轧过程中,所述钢的卷取温度高于630℃,然后在已知卷材中形成块状碳化物。如果在连续退火阶段从保持温度快速冷却至超过50℃/秒,则所述行进带材的随后货架处理温度在300℃至500℃的范围内至少保持10℃。冷却至室温后,将所述带材卷取,因此屈服点低于约23kg / mm 2,显示出延迟的老化性能和良好的可拉伸性。
展开▼