摘要
A method for the manufacture of high modules oxybenzoyl copolyester fibers which comprises: making a fiber from a moldable, film forming polyester having a molecular weight in the range of from 2,000-200,000 an a melting point of at least 250degrees C and comprising recurring moieties of the group of formulae I, II and III.wherein n is 0 or 1; x, y and z are integers; y:z=from 10:15 to 15:10, x:y and x:z=from 1:100 to 100:1; x+y+z=from 30 to 600; and the carbonyl group of formula I is meta and/or para to the oxy group thereof; the carbonyl groups of formula II are meta and/or para phi to each other; and the oxy atoms of formula III are meta and/or para to each other; with more than 50% of the total of said moieties having said mentioned groups therein of para configuration; heating the fiber at a temperature in the range of from about 250degrees C to about 500degrees C and stretching the fiber to increase the length thereof from about 10% to about 400% to increase the tensile strength and Young''s modulus.
展开▼
机译:一种用于制造高模量的氧苯甲酰基共聚酯纤维的方法,该方法包括:由分子量为2,000至200,000且熔点至少为250℃的可模塑成膜聚酯制成纤维,并包括式I,II和III的组。其中n为0或1; x,y和z是整数; y:z =从10:15到15:10,x:y和x:z =从1:100到100:1; x + y + z = 30至600;式I的羰基是其氧基的间位和/或对位;式II的羰基彼此为间和/或对位;式III的氧原子彼此间和/或对位;在所述部分的总数中有超过50%的其中所述的基团具有对位构型;在约250℃至约500℃范围内的温度下加热纤维,并拉伸纤维以将其长度从约10%增加至约400%,以增加拉伸强度和杨氏模量。
展开▼