Process for preparing titanium carbide base powder for cemented carbide alloys
Process for preparing titanium carbide base powder for cemented carbide alloys
展开▼
机译:硬质合金合金的碳化钛基粉的制备方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
A process comprises the steps of molding a mixture of usual TiC powder material having a combined carbon content lower than the theoretical value and a required amount of binder metal, sintering the molded mixture at a high temperature of about 1550° to 2500° C, and maintaining the sintered product at the high temperature, whereby the combined carbon content is increased to the highest possible value approximate to the theoretical value and the binder metal is fully effectively fused to the surface of the TiC particles. The resulting product is readily crushable to a powder having greatly improved amenability to sintering.