NOVEL LOW TEMPERATURE MATURING DENTAL GLAZE
NOVEL LOW TEMPERATURE MATURING DENTAL GLAZE
展开▼
机译:新型低温加工牙齿釉
展开▼
页面导航
摘要
著录项
相似文献
摘要
The instant invention relates to a novel dental glaze which matures at a temperature of from 1400 DEG to 1600 DEG F, that is, at least 200 DEG lower than the vitrifying temperature of dental porcelain. The chemical composition of this novel glaze may be thusly represented, on a weight basis: }SiO2 45-52% }B2O3 15-20% }Al2O3 10-15% }K2O 3.5-7.5% }Na2O 12-17% }CaO 0-1% }ZnO 0-1% }F 1-3% } Preferably the instant novel glaze is further characterized as having an average particle size of 10 +/- 4 microns and not more than 1% of the particles having a diameter greater than 30 microns.