PREPARATION OF GRANULAR SODIUM TRIPOLYPHOSPHATE PRODUCTS FROM SCREEN UNDERSIZE SODIUM TRIPOLYPHOSPHATE PARTICLES
PREPARATION OF GRANULAR SODIUM TRIPOLYPHOSPHATE PRODUCTS FROM SCREEN UNDERSIZE SODIUM TRIPOLYPHOSPHATE PARTICLES
展开▼
机译:从筛分不足的磷酸三钠颗粒中制备颗粒状的磷酸三钠产品
展开▼
页面导航
摘要
著录项
相似文献
摘要
ABSTRACT:Screen undersize sodium tripolyphosphate (STPP)particles are compacted, milled and moisturized byadding a sufficient amount of water thereon to producea material containing on the average between about15% and about 35% by weight moisture. The moisturizedmaterial is calcined to a temperature within the rangeof from about 300 to about 600°C, to produce a granularSTPP product having a low friability, high absorptiv-ity, and a bulk density within the range of om about0.65 to about 0.87 g/cc.
展开▼
机译:抽象:筛分过小的三聚磷酸钠(STPP)颗粒被压实,研磨和润湿在其上添加足够量的水以产生平均含有约15%和约35%的水分。保湿将材料煅烧至温度范围内在约300至约600°C的温度下具有低脆性,高吸收率的STPP产品密度和在om范围内的堆积密度0.65至约0.87 g / cc。