Hot workability of age hardenable nickel base alloys
Hot workability of age hardenable nickel base alloys
展开▼
机译:时效硬化镍基合金的热加工性能
展开▼
页面导航
摘要
著录项
相似文献
摘要
Very significant improvements in the hot workability of an age hardenable nickel base alloy containing 14 to 20 percent chromium, 1.4 to 5.3 percent titanium, 1.2 to 4.7 percent aluminum, 8 to 22 percent cobalt, up to 10 percent molybdenum, up to 3.5 percent tungsten, 0.004 to 0.040 percent boron, 0.02 to 0.15 percent carbon and about 52 to about 62 percent nickel are achieved by melting the raw materials under vacuum in the presence of lime, and forming a desulfurizing lime slag on the surface of the molten raw materials, and thereafter adding magnesium thereto just prior to casting the alloy, preferably while maintaining the molten raw material under an inert gas atmosphere.