COMPOSITION AND PROCESS FOR THE ELECTRO-DEPOSITION OF ZINC-NICKEL ALLOY DEPOSITS
COMPOSITION AND PROCESS FOR THE ELECTRO-DEPOSITION OF ZINC-NICKEL ALLOY DEPOSITS
展开▼
机译:锌镍合金镀层的电沉积组成及工艺
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE: To provide a Zn-Ni alloy plating soln. having improved gloss and throwing power by contg. zinc chloride, nickel chloride and ammonium chloride in such a way as to contain Zn2+, Ni2+, NH4+ at specific concns. and contg. specific surfactants. CONSTITUTION: A Zn-Ni alloy electroplating soln. contg. zinc chloride, nickel chloride and ammonium chloride so as to contain 10W90g/l Zn2+, 5W60g/l Ni2+ and 5W120g/l NH4+ and contg. ?2.5 Zn2+/Ni2+ (by weight) and further contg. a surfactant having polyoxyalkylene chains is prepd. There are polyoxyethylene alkyl ether, etc. for the surfactant having polyoxyalkylene chains, and usually the surfactant is added at about 0.1W200g/l. The pH of the plating soln. is controlled to 4.7W8.0, and aryl aldehyde, etc. can be added at about 0.01W2g/l as a secondary brightenes[JP58034189A]
展开▼
机译:目的:提供一种锌镍合金电镀液。持续改善了光泽和投掷能力。氯化锌,氯化镍和氯化铵,使其在特定浓度下包含Zn2 +,Ni2 +,NH4 +。和续。特定的表面活性剂。组成:一种锌镍合金电镀液。续氯化锌,氯化镍和氯化铵,以便包含10W90g / l Zn2 +,5W60g / l Ni2 +和5W120g / l NH4 +和续。 ≤2.5Zn 2+ / Ni 2+(按重量计)并进一步续。制备具有聚氧化烯链的表面活性剂。具有聚氧化烯链的表面活性剂有聚氧乙烯烷基醚等,通常以约0.1W200g / l的量添加。电镀液的pH值。控制为4.7W8.0,并可以约0.01W2g / l的量添加芳基醛等作为次生光亮剂[JP58034189A]
展开▼