A procedure of preparing fiber and Fine denier or multifilaments, based on Ethylene copolymers
展开▼
机译:一种基于乙烯共聚物的纤维和细旦或复丝的制备方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
Preparation method of Fine denier Fibers and multifilaments, based on Ethylene copolymers. Is spinning in Fusion, in solution or in a compound at a temperature between 125th and 350jc C and a pressure of between 3.5 and 2.100 kg / cm2, a low density Ethylene Copolymer comprising at least one Alpha olefin of 3 to 12 carbon ATOMS, which has a density of 0.86 to 0.94 g / cm3, and a melt flow value of 0.01 to 400 g / 10 min, according to the ASTM D - 1238 (e).These Fibers have applications for Manufacturing internal surfaces for diapers, Sanitary Products, Medical Products, linen Fabrics, Industrial Fabrics and Networks, membranes, Filters, Ropes, etc.
展开▼
机译:基于乙烯共聚物的细旦纤维和复丝的制备方法。包含至少一种3至12个碳原子的ATOMS的低密度乙烯共聚物在Fusion中,在溶液中或在化合物中于125°C至350°C的温度和3.5至2.100 kg / cm2的压力下纺丝,根据ASTM D-1238(e),其密度为0.86至0.94 g / cm3,熔体流动值为0.01至400 g / 10分钟。这些纤维可用于制造尿布的内表面,卫生产品,医疗产品,亚麻织物,工业织物和网络,膜,过滤器,绳索等
展开▼