Use of weldable high strength Cr-Ni-Mo-Ti steel as a stainless construction steel for products having a high longevity
Use of weldable high strength Cr-Ni-Mo-Ti steel as a stainless construction steel for products having a high longevity
展开▼
机译:可焊接的高强度Cr-Ni-Mo-Ti钢用作高寿命产品的不锈钢结构钢
展开▼
页面导航
摘要
著录项
相似文献
摘要
The composition of the steel of the mixed structure of perlite with iron element is: the Mo of titanium up to 0.6% Ni 0.2 to 1.5% Cr 1.0 to 3.0% Mn 13.0 to 16.0% Si up to 2.0% C up to 1.Up to the 0. of 0%10% remainder life is pressed with common accompanying element, is at least 13.The total of 5% % Cr+% Mo. It is generated in the form of through the heat of the thermo-mechanical treatment process limited or cold-rolled forming section product, the combination of the high temperature deformation on the one hand limited, its with subsequent stress relief annealing in the case where the deformed end temperature or another aspect thermal deformation reduced in the range of 650 to 800 degrees Celsius under the control in 600 to 800 degrees Celsius of temperature range and annealed raw material cold deformation limits degree of deformation in the range of 10 to 30%, as a special steels, its 0. at least 420 N/ millimeters2or at least 600 N/ millimeters2of region for limiting differenceThe minimum value of 2 limits. Investment goods and cargo of the steel especially suitable for the long-life used in everyday, wherein requiring be coupled in good corrosion resistance one to increase intensity and bending strength and/or pressure mottling resistance.
展开▼
机译:珍珠岩与铁元素混合结构的钢的成分为:钛的Mo最高为0.6%Ni 0.2至1.5%Cr 1.0至3.0%Mn 13.0至16.0%Si最高为2.0%C最高为1.Up到0。0%剩余寿命的10%用共同的伴随元素压制,至少为13。总计5%%Cr +%Mo。它是通过热机械处理过程中的热量产生的有限或冷轧成型型材,一方面是高温变形的结合,另一方面是在变形的端部温度或其他方面热变形降低到650到800度的情况下,进行随后的应力消除退火摄氏温度控制在600至800摄氏度的温度范围内,并且经退火的原材料冷变形将变形度限制在10%至30%的范围内,作为特殊钢,其变形系数为0。至少420 N / mm 2或至少600 N / mm 2的区域用于极限差Th e最小值为2个限制。特别适合于每天使用的长寿命的投资货物和货物,其中要求以良好的耐腐蚀性结合以增加强度和弯曲强度和/或耐压纹性。
展开▼