1. Method for the depth reconstruction of buildings reinforced with structural steel, whereby the damaged concrete is bored to behind the corroded reinforcement, characterised in that the solution of an alkali silicate with an Me2 O : SiO2 ratio of 1:2 to 1:3 is pressed in through the bore under pressure and thereafter a cement/water wash with alkali silicate solution or a mortar mixture, which contains 2 to 6% by weight, relative to the proportion of cement, of a finely divided amorphous silicic acid containing at least 90% by weight SiO2 or finely divided, precipitated, active silicates of magnesium, calcium, barium or aluminium with a BET surface area of 50 to 200 m**2 /g and a d50 % value of under 20 mu m, is pressed in under pressure.
展开▼
机译：1.一种用结构钢加固的建筑物的深度重建方法，其中将损坏的混凝土钻孔到腐蚀的钢筋后面，其特征在于，Me 2 O∶SiO 2比为1∶2至1∶3的碱金属硅酸盐溶液在压力下将其压入孔中，然后用碱金属硅酸盐溶液或砂浆混合物进行水泥/水洗，所述水泥/水混合物相对于水泥的比例含有2至6重量％的细碎无定形硅酸，其中至少含有压入90％重量的SiO2或镁，钙，钡或铝的细碎，沉淀的活性硅酸盐，BET表面积为50至200 m ** 2 / g，d50％值小于20μm。在压力之下。
展开▼