Fine coagulated particles of ultrafine monoclinic zirconia crystals oriented in a fiber bundle-like form and method of manufacturing them

摘要

Coagulated particles of ultrafine monoclinic zicronia crystals oriented in fiber bundle-like form, wherein primary particles of ultrafine monoclinic zirconia are oriented to join and extended in the direction of C-axis into fine fibrous form of less than 50 diameter and they are further gathered into a bundle-like form having from 300 to 2000 of width and from 2000 to 10000 of length. Such particles are prepared by hydrothermal processing which is applied at a temperature from 120 to 300 C. to an acidic aqueous solution containing a water-soluble zirconium compound in an amount of from 0.1 to 2.0 mol/l as Zr, SO.sub.4.sup.2- in an amount of from 0.2 to 2.0 mol/l and a water-soluble compound selected from the group consisting of water-soluble magnesium compounds, water-soluble ammonium compounds and mixtures thereof in an amount of from 0.05 to 1.5 mol/l as Mg.sup.2+ or NH.sub.4.