process for improving the properties at high temperatures and the saldabilita of steel alloys modified by chromium molybdenum selected
process for improving the properties at high temperatures and the saldabilita of steel alloys modified by chromium molybdenum selected
展开▼
机译:铬钼改性钢合金的高温性能和耐碱性的改进方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
Forgings fabricated from 9 Chromium - 1 Molybdenum, modified alloys are subjected to tempering at a temperature less than the ASTM specified minimum tempering temperature in the range from about 1275 DEG F. to about 1300 DEG F. for a period of time in the range of from about 5 to about 20 hours to cause the forging to have a room temperature yield strength in the range from about 85 to about 100 ksi. Such room temperature yield strengths permit the use of the alloy in the fabrication of high-pressure steam turbine rotors. Forgings fabricated from such alloys possess excellent high-temperature properties and the same are also weldable to facilitate repair of rotors fabricated therefrom and to facilitate the fabrication of the rotor in the first instance by forming the rotor from smaller sections which may be welded together and subsequently tempered at a temperature in the range from about 1275 DEG F. to about 1300 DEG F.
展开▼