Gold-free cobalt, nickel, chromium alloy - for mixing with ceramics to produce dental parts, has good corrosion resistance
Gold-free cobalt, nickel, chromium alloy - for mixing with ceramics to produce dental parts, has good corrosion resistance
展开▼
机译:无金的钴,镍,铬合金-与陶瓷混合制成牙科零件,具有良好的耐腐蚀性
展开▼
页面导航
摘要
著录项
相似文献
摘要
Dental alloy comprises by wt.% 9-37 Ni, 18-25 Cr; max. 11 Mo, max. 22 W; max. 1 Ti; max. 3 Nb, max. 20 Fe; max. 2 Mn; max. 1.5 Al; max.1 Si; bal Co plus usual impurities. The Mo content (a) and W content (b) also fulfill the conditions 2a+b is between 12 and 22. Pref. it contains less than 0.1 wt.% C and has a termal expansion coefft. at 20-600 deg.C of 14 x 10 power -6/deg K- 14.6 x 10 power -6/deg.K. ADVANTAGE - For blending with ceramic to produce false teeth crowns and bridges. Free from noble metals. e.g. Au but has comparable corrosion resistance to high Au alloys. Is workable and is chemically compatible with the body.
展开▼
机译:牙科合金包含9-37重量%的Ni,18-25Cr;最高最大11 Mo 22瓦;最高1钛;最高最大3 Nb 20铁;最高2锰;最高1.5铝;最大1 Si; bal Co加通常的杂质。 Mo含量(a)和W含量(b)还满足条件2a + b在12至22之间。它含有少于0.1 wt。%的C,并具有热膨胀系数。在20-600摄氏度时为14 x 10幂-6 / deg K- 14.6 x 10幂-6 / degK。优点-与陶瓷混合制成假牙冠和牙桥。不含贵金属。例如金,但具有与高金合金相当的耐蚀性。可行并且与身体化学相容。
展开▼