Synthetic resin mixts. (I), which give dry, clear films after evapn. of solvent and harden at mild temp., are useful as binders for surface coatings and printing ink for gravure-, flexo-, and screen-printing. (I) comprises (a) aliphatic cpd(s). contg. more than 1 epoxide gp. (II), (b) amine derivs. of formula H2N(CHR)xNH2 (III), H2N((CHR)x-NH)yH (IV), H2N(CH2)n-O-(R'-O)z-(CH2)nNH2, 4-piperidyl-(CH2)xNH2 or 4-piperazinyl-(CH2)xNH2, R2N-R2-OH, or free amine gp.-contg. adducts of (II) with 1-1.2 mol/epoxy gp. of the above amine(s) and opt. up to 50 equiv.% of the last-cited tert. amine, (c) thermoplastic resins (V) with free COOH gps. and Acid No.40-200 (1-10 above amino gps. per COOH), (d) solvents, and (e) pigments, accelerators, and other usual additives as required. In the formulae, R = H or 1-4C alkyl; R' = opt. substd. 1-4C alkyl; R2 = (CRR)x or (CH2)2-O-(CH2)2; x = 2-6; y = 2-4; z = 0-3; n = 2-5. (I) are mfd. by successive addn. of amine, (II), and (V) to an alcohol/water (1:9) mixt. and heating to dissolve.
展开▼
机译：合成树脂混合物。 （I），蒸发后得到干燥，透明的薄膜。适量的溶剂并在温和的温度下硬化，可用作表面涂料的粘合剂和凹版，柔版和丝网印刷的印刷油墨。 （I）包括（a）脂族cpd。续环氧1 gp以上。 （II），（b）胺衍生物。式H2N（CHR）xNH2（III），H2N（（CHR）x-NH）yH（IV），H2N（CH2）nO-（R'-O）z-（CH2）nNH2、4-哌啶基-（CH2 ）xNH2或4-哌嗪基-（CH2）xNH2，R2N-R2-OH或游离胺gp.-contg。 （II）具有1-1.2 mol /环氧gp的加合物。上述胺的一种和选择。最高为最后引用的叔叔的50当量％。胺，（c）具有游离COOH gps的热塑性树脂（V）。 40-200号酸（每gCOOH，氨基gps高于1-10），（d）溶剂和（e）所需的颜料，促进剂和其他常用添加剂。式中，R ＝ H或1-4C的烷基。 R'=选择。取代1-4C烷基; R2 =（CRR）x或（CH2）2-O-（CH2）2; x = 2-6; y = 2-4; z = 0-3; n = 2-5。 （I）是MFD。通过连续添加。将胺，（II）和（V）混合成酒精/水（1：9）混合物。加热溶解。
展开▼