A method for the production of an extremely drawn polymeric material which, as well as a process for the production of optionally nsta ends.

摘要

An ultrastretchable polymer material is prepared starting from polyolefine particles with a low entanglement density and a weight average molecular weight (MW) higher than 400,000, the particles being densified to a coherent material together with a process auxiliary material at an elevated temperature, but below the melting point of the pure polyolefine. From this ultrastretchable material, objects with a high tensile strength and a high modulus can be produced by stretching it, for instance, at a temperature which is at most 70 DEG C below the temperature at which the polyolefine melts under the prevailing conditions, if desired after removal of the process auxiliary agent present in it.