MN-ZN FERRITE TEMPORARY BAKED POWDER FOR OBTAINING CORE WITH HIGH SATURATION MAGNETIC FLUX DENSITY AND LOW LOSS
MN-ZN FERRITE TEMPORARY BAKED POWDER FOR OBTAINING CORE WITH HIGH SATURATION MAGNETIC FLUX DENSITY AND LOW LOSS
展开▼
机译:用于获得高饱和磁通量密度和低损耗的核的MN-ZN铁素体临时烘烤粉末
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE: To obtain a core having high density and excellent electromagnetic characteristics by limiting a mean primary particle size and mean secondary particle size of temporary baked powder to specific ranges. ;CONSTITUTION: Fe2O3, MnO and ZnO are so weighed as to become 71, 22 and 7wt.%, 150, 500ppm of SiO2 and CaO are added thereto, and mixed by a ball mill. The mixture is temporarily baked at 950-1000°C for 1 hour to manufacture ferrite powder having a mean primary particle size of 0.13-1.0μm. Then, it is pulverized by a wet ball mill using pure water as solvent, and Mn-Zn ferrite having a mean secondary particle size (50% particle size) of a range of 1.0-1.4μ is manufactured. When the powder obtained in this manner is used, a sintered material having high sintering density, and fine and uniform crystalline grain composition is obtained, and hence a soft ferrite core having high saturation magnetic flux density and low core loss can be stably manufactured.;COPYRIGHT: (C)1994,JPO&Japio
展开▼
机译:目的:通过将临时烘烤粉末的平均一次粒径和平均二次粒径限制在特定范围内,以获得具有高密度和优异电磁特性的核。 ;组成:Fe 2 Sub> O 3 Sub>,MnO和ZnO的称量比例分别为SiO 2的71、22和7wt。%,150、500ppm。将Sub>和CaO加入其中,并通过球磨机混合。将该混合物在950-1000℃下临时烘烤1小时,以制造平均一次粒径为0.13-1.0μm的铁氧体粉末。然后,使用纯水作为溶剂,通过湿式球磨机进行粉碎,从而制造出平均二次粒径(50%粒径)为1.0〜1.4μ的范围的Mn-Zn铁氧体。当使用以此方式获得的粉末时,具有高烧结密度的烧结材料,并且获得了细而均匀的晶粒组成,因此可以稳定地制造具有高饱和磁通密度和低铁损的软铁氧体磁芯。版权所有:(C)1994,JPO&Japio
展开▼