SEPARATOR FOR SEALED LEAD-ACID BATTERY AND ITS MANUFACTURE AND SEALED LEAD-ACID BATTERY
SEPARATOR FOR SEALED LEAD-ACID BATTERY AND ITS MANUFACTURE AND SEALED LEAD-ACID BATTERY
展开▼
机译:密封铅酸蓄电池的分离器及其制造和密封铅酸蓄电池
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE:To produce a separator which can retain increased amount of an electrolytic solution and has improved high discharge efficiency for a lead-acid battery by throwing small pieces of entangled glass short fibers in water, dispersing them, and forming into a sheet. CONSTITUTION:Entangled, alkali-resistant silicate glass short fibers are adjusted to be 3-10mm fiber length and thrown to water. Then, they are dispersed in the water by a dispersing and mixing apparatus without being loosened by a heater and formed into a paper by a paper machine. As a result, a paper-like separator with 9-15% tensile expansion and 0.11-0.14g/cm3 density is obtained, battery capacity and discharge characteristics are increased, electrolytic solution is uniformly retained, a layer formation ratio preventive effect is produced, and then a sealed lead-acid battery separator prolonging the battery life is manufactured.
展开▼
机译:用途:生产一种隔膜,该隔膜可以将少量缠结的玻璃短纤维放入水中,分散并制成片,从而可以保留更多的电解液并提高铅酸电池的高放电效率。组成:缠结,耐碱的硅酸盐玻璃短纤维被调整为3-10mm的纤维长度,并投入水中。然后,它们通过分散和混合设备分散在水中,而没有被加热器弄松,而是通过造纸机形成纸。结果,获得了具有9-15%的拉伸膨胀和0.11-0.14g / cm 3密度的纸状隔板,电池容量和放电特性提高,电解质溶液被均匀地保留,防止层形成率制造铅,然后制造可延长电池寿命的密封铅酸电池隔膜。
展开▼