A lanthanum chromite ceramic powder consisting essentially of 1 mol of LaCr1-xMxO3, where M is a divalent metal selected from the group of zinc, copper and mixtures thereof and x ranges from about 0.02 to 0.2, y mols of B2O3, where y ranges from 0.0005 to 0.04, and z mols of La2O3, where the ratio z/y ranges from 1 to 3, the powder is sintered to high density by firing a compact thereof at a temperature of about 1400 degrees C. in air or other atmosphere, and is particularly suited for use as interconnect material for solid oxide fuel cells.
展开▼
机译:一种亚铬酸镧陶瓷粉末,主要由1摩尔LaCr1-xMxO3组成,其中M是选自锌,铜及其混合物的二价金属,x为0.02到0.2,y摩尔为B2O3,其中y为0.0005至0.04,以及z摩尔La 2 O 3(其中z / y比为1至3),通过在空气或其他气氛中在约1400℃的温度下将其压坯烧成粉末来将粉末烧结至高密度,并且特别适合用作固体氧化物燃料电池的互连材料。