ALUMINUM ALLOY SHEET HAVING BLUISH GRAY COLOR TONE AFTER ANODIC OXIDATION TREATMENT AND ITS PRODUCTION
ALUMINUM ALLOY SHEET HAVING BLUISH GRAY COLOR TONE AFTER ANODIC OXIDATION TREATMENT AND ITS PRODUCTION
展开▼
机译:铝合金阳极氧化处理后呈灰色灰色的铝合金板材及其生产。
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE: To produce a rolled sheet having a bluish dark gray color tone reduced in a tinge of yellow after anodic oxidation treatment. ;CONSTITUTION: This sheet is a rolled Al alloy sheet which consists of 1.2-5.5% Mg, 0.3-0.8% Mn, 0.0040-0.05% Ga, ≤0.5% Fe, ≤0.2% Si, ≤0.2% Cr, 0.003-0.20% Ti (combining 1 to 100ppm B), and the balance Al with inevitable impurities and in which Al6Mn or Al6(MnFe) having 0.05-1.5μm size is dispersed at (5×10 to 1×107)pieces/mm density. The alloy is cast, preheated at 400-600°C for 0.5-24hr, and further heated, prior to hot rolling, at 350-530°C for 0.5-24hr, by which an Al-Mn intermetallic compound is precipitated. Then, primary cold rolling, process annealing, and final cold rolling are performed.;COPYRIGHT: (C)1996,JPO