PREPARING PROCESS FOR COMPLEX DRAWING TEXTURED YARN HAVING IMPRESSING HEMP
PREPARING PROCESS FOR COMPLEX DRAWING TEXTURED YARN HAVING IMPRESSING HEMP
展开▼
机译:具有麻感的复杂拉伸丝纱线的制备工艺
展开▼
页面导航
摘要
著录项
相似文献
摘要
The polyester finished yarn is made by pre-untwisting yarn obtained from partially oriented polyester yarn(POY). The pre-untwisting yarn has a filament fineness of grey yarn in the range of 1.6= d.p.f= 3.4 and a draw ratio of 1.250= D/R= 1.450, which is passed through the first heater at 220-247 deg.C and second heater at 190-230 deg.C to give the finished yarn. The finished yarn has a good shari feeling.
展开▼
机译:聚酯成品纱线是通过将由部分取向的聚酯纱线(POY)制成的纱线预解捻制成的。预解捻纱的灰纱长丝纤度在1.6 = dpf = 3.4范围内,拉伸比为1.250 = D / R = 1.450,在220-247℃时通过第一加热器,第二在190-230℃下加热以得到成品纱线。制成的纱线具有良好的纱丽感。