Manufacturing method of Bi-xPbySrCa.CuOz high-temperature superconductor
Manufacturing method of Bi-xPbySrCa.CuOz high-temperature superconductor
展开▼
机译:Bi-xPbySrCa.CuOz高温超导体的制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
SUMMARY OF THE INVENTION [2-xPbySr2Ca2.2Cu3The present invention relates to a method for producing a high-temperature superconductor, and more particularly, to a method for manufacturing a high-temperature superconductor, comprising the steps of: weighing Bi, Pb, Sr, Ca, and Cu nitrate in a cation ratio of 2-x: y: 2: 2.2: 3 (x, y = 0.2-0.4) After dissolving, Bi-2223 precursor powders were prepared by using a spray drier, and the powders were calcined at 800 to 820C for 3 hours or more and heat-treated at 830 to 850C for 30 to 100 hours Bi-2223 A method for manufacturing a high-temperature superconductor.
展开▼
机译:发明内容[ 2 Sub> -xPbySr 2 Sub> Ca 2.2 Sub> Cu 3 Sub>本发明涉及一种制备方法高温超导体的制造方法,更具体地说,涉及一种高温超导体的制造方法,该方法包括以下步骤:以2-x:y:2的阳离子比称重Bi,Pb,Sr,Ca和Cu硝酸盐。 :2.2:3(x,y = 0.2-0.4)溶解后,使用喷雾干燥器制备Bi-2223前体粉末,并将该粉末在800-820℃下煅烧3小时以上,并在830-230℃下进行热处理。 850℃30到100个小时Bi-2223一种制造高温超导体的方法。
展开▼