Titanium - graphite a sintered material with improved wear resistance and a low coefficient of friction

摘要

A process for producing sintered titanium-graphite having improved wear resistance and low frictional characteristics is described. The said process which produces titanium-graphite composites having a triphasic structure with controlled porosity and a graphite lubricating film, comprises sintering a mixture of titanium and graphite powders in which the percentage of graphite may vary from 4 to 8 percent at temperatures from about 800 DEG C. to 1600 DEG C., for about +E,fra 1/2+EE to 2 hours, under a compaction pressure of 0.17 to 0.62 MPa. The composites have applications in biomedical engineering and other fields of engineering due to their biocompatibility, strength and improved wear resistance.