NONWOVEN FABRIC OR WOVEN OR KNITTED FABRIC HAVING THERMALLY BONDED CROSSING PART OF WARP AND WEFT AND LAMINATE USING THE SAME
NONWOVEN FABRIC OR WOVEN OR KNITTED FABRIC HAVING THERMALLY BONDED CROSSING PART OF WARP AND WEFT AND LAMINATE USING THE SAME
展开▼
机译:非织造布或机织或针织的布具有热粘合的经线和纬线交叉部分,并且使用相同的层压材料
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To obtain a nonwoven fabric/woven or knitted fabric excellent in bond strength, causing neither shifting nor deformation. ;SOLUTION: A lamination type or a sheath-core type yarn comprising a first polyolefin resin based resin 1 and a second low-melting polyolefin-based resin 2 is laminated, or woven or knitted and crossing parts of warp and weft are thermally bonded. The second polyolefin-based resin 2 is an ethylene/α-olefin copolymer which is obtained by copolymerizing ethylene with an α-olefin by using a metallocene catalyst and has 0.1-30g/10 minutes MFR, 0.87-0.93g/cm3 density, 70-125°C maximum peak temperature, 1.8-3 molecular weight distribution and 0.5-4g melt tension.;COPYRIGHT: (C)1998,JPO
展开▼
机译:解决的问题:获得粘合强度优异,既不会移动也不变形的无纺布/机织或针织物。 ;解决方案:将包含第一聚烯烃树脂基树脂1和第二低熔点聚烯烃基树脂2的层压型或皮芯型纱线层压在一起,或进行机织或编织,并将经纱和纬纱的交叉部分热粘合。第二聚烯烃基树脂2是乙烯/α-烯烃共聚物,其通过使用茂金属催化剂使乙烯与α-烯烃共聚而获得,并且具有0.1-30g / 10分钟的MFR,0.87-0.93g / cm 2。 3 Sup>密度,70-125°C最高峰值温度,1.8-3分子量分布和0.5-4g熔体张力。;版权所有:(C)1998,日本特许厅
展开▼