PURPOSE:To obtain the subject copolymer having specific composition, crystallinity, melt index and elastic modulus and high heat-resistance, solvent resistance and crosslinking efficiency and giving a crosslinked product having excellent tensile properties and abrasion properties by copolymerizing an alpha-olefin with a specific non-conjugated diene, etc. CONSTITUTION:The objective random copolymer having a non-conjugated diene content of 0.1-15mol%, a crystallinity of =20% (by X-ray diffraction), a melt- index of 0.01-200g/10min and an elastic modulus of 1,000-30,000kg/cm2 (measured in conformity to JIS K7203) can be produced by copolymerizing (A) at least one kind of 3-12C alpha-olefin (e.g. propylene), (B) at least one kind of non- conjugated diene of formula (R1 is 1-8C alkyl; R2 to R5 are H or 1-8C alkyl; (n) is 2-10) (e.g. 7-methyl-1,6-octadiene) and, as necessary, (C) ethylene in the presence of (D) a catalyst comprising triethylaluminum, etc.
展开▼
机译:目的:获得具有特定组成,结晶度,熔体指数和弹性模量以及高耐热性,耐溶剂性和交联效率的主题共聚物,并通过将α-烯烃与特定烯烃共聚,得到具有优异拉伸性能和耐磨性的交联产物。组成:非共轭二烯含量为0.1-15mol%,结晶度> = 20%(通过X射线衍射),熔融指数为0.01-200g /通过使(A)至少一种3-12C的α-烯烃(例如丙烯),(B)共聚,可以制造10分钟,弹性模量为1,000-30,000kg / cm 2(根据JIS K7203测量)。至少一种式(R 1为1-8C烷基; R 2至R 5为H或1-8C烷基;(n)为2-10)的非共轭二烯(例如7 -甲基-1,6-辛二烯)和(C)乙烯,必要时在(D)有三乙基铝等的催化剂存在下。
展开▼