METHOD FOR MANUFACTURING B4C, TITANIUM-ALUMINA COMPLEX BY SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS
METHOD FOR MANUFACTURING B4C, TITANIUM-ALUMINA COMPLEX BY SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS
展开▼
机译:自蔓延高温合成制备B4C,钛铝配合物的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
In the present invention, a preform prepared under a constant pressure by mixing B 2 O 3 powder, Mg powder, and carbon black is placed in a self-burning reactor, and chemically modified TiO 2 / Al / C is first used from the outside. After the ignition, the method for producing a B 4 C powder characterized in that the autogenous combustion reaction of B 2 O 3 / Mg / C by the exotherm.;In addition, in the present invention, TiO 2 / Al / C used as a chemical furnace is mixed in a molar ratio of 2-3: 3-5: 2-4, placed outside the pellet of B 2 O 3 / Mg / C and reacted to B 4 The present invention relates to a method for producing a titanium-alumina composite, characterized in that C powder is prepared and the pellet is pulverized by the reaction terminated chemistry to produce TiC / Al 2 O 3 , which can be used as a preform of the composite material.
展开▼
机译:在本发明中,将通过混合B 2 Sub> O 3 Sub>粉末,Mg粉末和炭黑在恒压下制备的预成型坯置于自燃反应器中,并且首先从外部使用化学改性的TiO 2 Sub> / Al /C。点火后,制备B 4 Sub> C粉末的方法,其特征在于B 2 Sub> O 3 Sub> / Mg / C的自燃反应另外,在本发明中,以2-3:3-5:2-4的摩尔比混合用作化学炉的TiO 2 Sub> / Al / C。放置在B 2 Sub> O 3 Sub> / Mg / C的颗粒外部并与B 4 Sub>反应的方法本发明涉及一种钛的生产方法。 -氧化铝复合材料,其特征在于制备C粉,并通过反应终止化学方法将其粉碎,生成TiC / Al 2 Sub> O 3 Sub>,可用作复合材料的预成型件。
展开▼