long glass fiber reinforced polypropylene mixture, and polypropylenharz and resulting molded parts
long glass fiber reinforced polypropylene mixture, and polypropylenharz and resulting molded parts
展开▼
机译:长玻璃纤维增强聚丙烯混合物,聚丙烯原胶和成型零件
展开▼
页面导航
摘要
著录项
相似文献
摘要
A mixture for melt process moldings, and a molding formed of the mixture. The mixture consists essentially of about 5 to about 70 wt% of a master batch prepared in the form of pellets formed by cutting a long glass fiber reinforced polypropylene resin, and about 30 to about 95 wt% of polypropylene resin. The long glass fiber reinforced polypropylene resin is prepared in such a manner that a bundle of continuous reinforcement glass fibers surface-finished with a finishing agent containing a coupling agent is impregnated with a modified polypropylene resin having a functional group capable of chemically bonding with the coupling agent and having a melt flow rate of about 70 to about 300 g/10 min (ASTM D-1238, load: 2.16 kg, temperature: 230 DEG C) while the bundle of glass fibers is being drawn. The pellets have a length of about 2 to about 50 mm in the direction along the fibers. The glass fibers in the pellets extend uniformly in parallel with each other through a distance substantially equal to the length of the pellets. The pellets have a glass fiber content of about 60 to about 90 wt%.
展开▼
机译:用于熔融加工模制品的混合物,以及由该混合物形成的模制品。该混合物主要由约5至约70重量%的通过切割长玻璃纤维增强的聚丙烯树脂而形成的粒料形式的母料和约30至约95重量%的聚丙烯树脂组成。长玻璃纤维增强聚丙烯树脂的制备方法是,将一束用含偶联剂的整理剂表面精加工的连续增强玻璃纤维浸渍在具有能够与偶联剂化学键合的官能团的改性聚丙烯树脂上。在拉制玻璃纤维束时,熔体的流动速率为约70至约300 g / 10 min(ASTM D-1238,载荷:2.16 kg,温度:230℃)。粒料在沿着纤维的方向上具有约2至约50mm的长度。粒料中的玻璃纤维彼此平行地均匀地延伸基本上等于粒料长度的距离。粒料的玻璃纤维含量为约60至约90重量%。
展开▼