PROBLEM TO BE SOLVED: To obtain a nonwoven fabric structural form comprising fluorine-based fibers and having both heat resistance and chemical resistance by removing, from a nonwoven fabric comprising a combination of the fluorine-based fibers and decomposable and/or dissolution-removable fibers, the latter fibers followed by subjecting the resultant fabric to high-pressure water jet interlacing treatment.;SOLUTION: This nonwoven fabric structural form comprising fluorine-based fibers is obtained by the following process: a nonwoven fabric is first produced by mixing fluorine-based fibers (e.g. fluoroethylene-based fibers) with decomposable and/or dissolution-removable fibers (e.g. polyvinyl alcohol-based fibers ≤90°C in underwater dissolution temperature or polyester fibers dissolvable in an aqueous alkaline solution) in a weight ratio of (50:50) to (95:5), pref. (60:40) to (90:10) followed by passing the mixture through a carding process, and the latter fibers are then removed from the nonwoven fabric followed by subjecting the resultant nonwoven fabric to water jet interlacing treatment at a hydraulic pressure of ≥50 kg/mm2.;COPYRIGHT: (C)2000,JPO
展开▼
机译:解决的问题:通过从包含氟基纤维和可分解和/或可溶解去除的纤维的组合的无纺布中去除,来获得包含氟基纤维并且具有耐热性和耐化学性的无纺布结构形式。解决方案:此含氟基纤维的无纺布结构形式是通过以下过程获得的:首先通过混合氟基纤维来生产无纺布具有可分解和/或可溶解去除的纤维(例如在水下溶解温度下≤90°C的聚乙烯醇基纤维或可溶于碱性水溶液的聚酯纤维)的纤维(例如氟乙烯基纤维)或重量比为(50: 50)至(95:5),优选。 (60:40)至(90:10),然后使混合物经过梳理过程,然后从无纺布中除去后者的纤维,然后在≥6%的水压下对所得的无纺布进行水射流交织处理。 50 kg / mm2 .;版权:(C)2000,JPO
展开▼