Composition for hindering the formation of iron oxides in steel-melting slag and EAF scrap- based steelmaking process using the same
Composition for hindering the formation of iron oxides in steel-melting slag and EAF scrap- based steelmaking process using the same
展开▼
机译:用于阻止在钢渣中的氧化铁形成的成分以及使用该成分的基于电弧炉废钢的炼钢工艺
展开▼
页面导航
摘要
著录项
相似文献
摘要
A composition comprising from 35 to 50 wt-% of C, from 10 to 20 wt-% of Al, from 25 to 40 wt-% of Al2O3, from 0 to 3 wt-% of CaO and from 0 to 3 wt-% of MgO, provided however that the combined amount of CaO and MgO is of from 1 to 6%. A process for preparing such composition as well as a process for using such composition in the melting of scrap iron in an electric furnace with the aim of decreasing iron losses due to oxidation and of lowering iron oxide content of steel melting slag.
展开▼
机译:一种组合物,其包含35至50重量%的C,10至20重量%的Al,25至40重量%的Al 2 Sub> O 3 Sub>, CaO和MgO的总含量为1至6%,但是CaO和MgO的总含量为0至3重量%,MgO为0至3重量%。制备这种组合物的方法以及在电炉中在废铁的熔融中使用这种组合物的方法,目的是减少由于氧化引起的铁损失并降低钢熔渣的氧化铁含量。