PREPARATION METHOD OF ANHYDROUS CALCIUM SILICATE AND ANHYDROUS CALCIUM ALUMINA SILICATE USING CALCIUM OXIDE OR CALCIUM HYDROXIDE, BY HEATING AT HIGH TEMPERATURE
PREPARATION METHOD OF ANHYDROUS CALCIUM SILICATE AND ANHYDROUS CALCIUM ALUMINA SILICATE USING CALCIUM OXIDE OR CALCIUM HYDROXIDE, BY HEATING AT HIGH TEMPERATURE
展开▼
机译:氧化钙或氢氧化钙通过高温加热制备无水硅酸钙和无水硅酸铝钙的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
Purpose: providing the above method and prepare anhydrous calcium silicates and anhydrous calcium aluminium hydrosilicate, obtains the porous material with good high temperature resistant, insulation and voice testing by recycling waste. Construction: anhydrous calcium silicates (CaO-nSiO2) forms mixture preparation by mixing CaO, Ca (OH) 2 and SiO2; In 700-1.050C.At a temperature of the heating anhydrous calcium aluminium hydrosilicate (CaO-mAl2O3-nSiO2) of mold body by mixing CaO, Ca (OH) 2, aluminium oxide, Al (OH) 3 and SiO2, form mixture preparation; In 800-1,350C.At a temperature of heat mold body