Polyethylene resin - composition for heavy load packaging bag and polyethylene resin film has produced therefrom
Polyethylene resin - composition for heavy load packaging bag and polyethylene resin film has produced therefrom
展开▼
机译:聚乙烯树脂-用于生产重载包装袋的组合物和聚乙烯树脂薄膜
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE: To obtain a polyethylene resin compsn. for heavy-duty packaging bag which is excellent in strengths, stiffness, and gloss and has improved low- temp. characteristics, esp. an improved low-temp. bag dropping strength, by compounding a specific linear low-density PE resin, a linear medium- to highdensity PE resin, and a high-pressure low-density PE resin. ;CONSTITUTION: This compsn. comprises 40-70wt.% linear low-density PE resin which is an ethylene-α-olefin copolymer obtd. by copolymerizing ethylene and 1-10mol% 4C or higher a-olefin using a metallocene catalyst and has a melt flow rate (190°C) of 0.1-1.0g/10min. a density of 0.900-0.918 g/cm3, and a mol. wt. distribution (Mw/Mn) by GPC of 1.5-3.5, 1-55wt.% linear medium- to high- density PE resin which is an ethylene homopolymer or a copolymer of ethylene and 10mol% or lower 3-20C a-olefin and has a density of 0.935-0.970g/cm3, and 5-29wt.% high-pressure low-density PE resin which is an ethylene homopolymer or a copolymer of ethylene and 2-10mol% vinyl acetate and has a density of 0.915-0.924g/cm3.;COPYRIGHT: (C)1996,JPO
展开▼
机译:目的:获得聚乙烯树脂复合物。适用于强度,刚度和光泽度极佳的低温重型包装袋。特征,特别是改进的低温。通过混合特定的线性低密度PE树脂,线性中高密度PE树脂和高压低密度PE树脂,可降低袋子的落袋强度。 ;组成:此组件。包含40-70重量%的线性低密度PE树脂,其为乙烯-α-烯烃共聚物。通过使用茂金属催化剂使乙烯与1-10mol%的4C或更高的α-烯烃共聚,其熔体流动速率(190℃)为0.1-1.0g / 10min。密度为0.900-0.918 g / cm 3 Sup>,且摩尔重量1.5-3.5、1-55wt。%线性中高密度PE树脂的GPC分布(Mw / Mn),为乙烯均聚物或乙烯与10mol%或更低的3-20Cα-烯烃的共聚物密度为0.935-0.970g / cm 3 Sup>,以及5-29wt。%的高压低密度PE树脂,它是乙烯均聚物或乙烯与2-10mol%的乙酸乙烯酯的共聚物,密度为0.915-0.924g / cm 3 Sup> .;版权:(C)1996,日本特许厅
展开▼