Extrusion-foamed board of resin blend comprising modified polypropylene resin and polystyrene resin
Extrusion-foamed board of resin blend comprising modified polypropylene resin and polystyrene resin
展开▼
机译:包含改性聚丙烯树脂和聚苯乙烯树脂的树脂共混物的挤出发泡板
展开▼
页面导航
摘要
著录项
相似文献
摘要
There is provided a foamed article having a low density, large thickness, a high closed cell ratio and a small average cell diameter. A foamed extrusion article having a density of 50 to 10 kg/m3 and a closed cell ratio of at least 40% is obtained by mixing a mixed resin comprising (a) 50 to 95 parts by weight of a polypropylene resin having a melt tension at 230° C. of at least 0.05 N, (b) 50 to 5 parts by weight of a polystyrene resin, and (c) 0.5 to 15.0 parts by weight of a hydrogenated block copolymer of styrene, isoprene and styrene based on 100 parts by weight of the polypropylene resin (a) and the polystyrene resin (b) with a foaming agent in an extruder, and then releasing into a low-pressure zone.
展开▼
机译:提供了一种具有低密度,大厚度,高闭孔率和小平均孔直径的泡沫制品。通过混合包含(a)50至95重量份的丙烯酸的混合树脂,获得密度为50至10kg / m Sup 3且闭孔率至少为40%的泡沫挤出制品。熔融张力为230℃的聚丙烯树脂。 C.基于100重量份的C,至少0.05 N,(b)50至5重量份的聚苯乙烯树脂和(c)0.5至15.0重量份的苯乙烯,异戊二烯和苯乙烯的氢化嵌段共聚物将聚丙烯树脂(a)和聚苯乙烯树脂(b)与发泡剂在挤出机中,然后释放到低压区。
展开▼