COLD TOOL STEEL HAVING CONSTANT DEFORMATION ON TREATMENT AND METHOD FOR PRODUCING COLD TOOL USING THE STEEL
COLD TOOL STEEL HAVING CONSTANT DEFORMATION ON TREATMENT AND METHOD FOR PRODUCING COLD TOOL USING THE STEEL
展开▼
机译:具有恒定变形的冷轧工具钢及其制造冷轧工具的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a cold tool steel which has a constant deformation on heat treatment, does not require finish working for removing the formation after quenching and has hardness of ≥55 HRC required as a die.;SOLUTION: The cold tool steel has a composition consisting of, by weight, 0.4 to 1.2% C, 0.1 to 1.2% Si, 0.3 to 2.0% Mn, 3.0 to 10.0% Cr and 0.5 to 3.0% Mo, and the balance substantially Fe. The composition is controlled so that pearlite nose is shorter than 250 min, and hardness is ≥55 HRC at the cooling rate of 2 to 50°C/min in quenching by gas cooling.;COPYRIGHT: (C)2002,JPO