REINFORCED COMPOSITE FIBER CERAMICS AND INFILTRATED OF CASTED METAL AND PROCEDURE FOR THE MANUFACTURE OF THE SAME.
REINFORCED COMPOSITE FIBER CERAMICS AND INFILTRATED OF CASTED METAL AND PROCEDURE FOR THE MANUFACTURE OF THE SAME.
展开▼
机译:增强的复合纤维陶瓷材料和浸渗的铸造金属及其制造工艺。
展开▼
页面导航
摘要
著录项
相似文献
摘要
The invention relates to composite ceramics reinforced with fibers infiltrated with molten metal and comprising high temperature resistant fibers, in particular based on Si / C / B / N, which are attached to a matrix based on Si, by reaction. The invention also relates to a method of manufacturing said ceramics. The silicon used for the infiltration contains additions of iron, chromium, titanium, molybdenum, nickel or aluminum, preferably the ground silicon contains approximately 5 to 50% by weight of iron and approximately 1 to 10% by weight of chromium. The manufacturing process is simpler than conventional ground silicon processes and confers improved properties to composite ceramics.
展开▼
机译:本发明涉及一种复合陶瓷,该复合陶瓷用浸入熔融金属的纤维增强并且包含耐高温纤维,特别是基于Si / C / B / N的耐高温纤维,所述耐高温纤维通过反应附接到基于Si的基质上。本发明还涉及一种制造所述陶瓷的方法。用于渗透的硅包含铁,铬,钛,钼,镍或铝的添加物,优选地,研磨的硅包含按重量计约5%至50%的铁和按重量计约1%至10%的铬。制造工艺比常规的研磨硅工艺更简单,并赋予复合陶瓷更高的性能。
展开▼