Glass ionomer-based fluoride applying material
Glass ionomer-based fluoride applying material
展开▼
机译:玻璃离聚物基氟化物涂覆材料
展开▼
页面导航
摘要
著录项
相似文献
摘要
A glass ionomer-based fluoride applying material that is able to release 200 mu g/cm2 or more, and preferably 300 mu g/cm2 or more of a fluoride ion until 30 days after immersing a set material thereof in distilled water kept at 37 DEG C, is provided, which contains a fluoroaluminosilicate glass powder, a polycarboxylic acid and water as major components, the fluoroaluminosilicate glass powder accounting for 5 to. 70 % by weight of the whole, preferably containing, as constitutional elements, 10 to 20 % by weight of Si, 10 to 20 % by weight of Al, 1 to 20 % weight of F, and 5 to 30 % by weight of Sr, and additionally, at least one of Na, K, Mg and Ca, and preferably containing Na in an amount of 3 to 15 % by weight.
展开▼
机译:一种玻璃离聚物基氟化物施加材料,在将其固化材料浸入其中30天后,它能够释放200μg / cm 2以上,优选为300μg / cm 2以上的氟离子。提供保持在37℃的蒸馏水,该蒸馏水包含氟铝硅酸盐玻璃粉末,多元羧酸和水作为主要成分,氟铝硅酸盐玻璃粉末占5%。占整体的70重量%,优选包含10至20重量%的Si,10至20重量%的Al,1至20重量%的F和5至30重量%的Sr作为构成元素以及另外,Na,K,Mg和Ca中的至少一种,并且优选含有3至15重量%的Na。
展开▼