CRYSTALLIZED GLASS FOR BUILDING MATERIAL HAVING NATURAL MARBLY PATTERN AND MANUFACTURING METHOD THEREOF
CRYSTALLIZED GLASS FOR BUILDING MATERIAL HAVING NATURAL MARBLY PATTERN AND MANUFACTURING METHOD THEREOF
展开▼
机译:具有天然大理石花纹的建筑用结晶玻璃及其制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
In the crystallized glass of the present invention, sodium sulfate is used as a cleaning agent, and by weight percentage, 45 to 77% SiO 2 , 1 to 25% A1 2 O 3 , CaO 2 to 25%, ZnO 0 to 18%, and BaO 0 to 20% , Na 2 O 1-15%, K 2 O 0-7%, Li 2 O 0-5%, B 2 O 3 0-1.5%, CeO 2 0.01-0.5%, SO 3 0.01-0.5% The glass raw materials so combined are melted and molded, and then crystallized. The crystallized glass of the present invention does not contain As 2 O 3 and Sb 2 O 3 , but is excellent in solubility and has good production efficiency, and has a whiteness equivalent to or higher than that of a conventional product.
展开▼
机译:在本发明的微晶玻璃中,使用硫酸钠作为清洁剂,以重量百分比计,SiO 2 Sub>为45%至77%,Al 2 Sub>为1%至25% O 3 Sub>,CaO 2至25%,ZnO 0至18%,BaO 0至20%,Na 2 Sub> O 1-15%,K 2 < / Sub> O 0-7%,Li 2 Sub> O 0-5%,B 2 Sub> O 3 Sub> 0-1.5%,CeO 2 Sub> 0.01-0.5%,SO 3 Sub> 0.01-0.5%将如此组合的玻璃原料熔融成型,然后结晶。本发明的微晶玻璃不含As 2 Sub> O 3 Sub>和Sb 2 Sub> O 3 Sub>,但含有溶解性优异,具有良好的生产效率,并且白度等于或高于常规产品。
展开▼