Case hardening steel with excellent prevention of the secondary recrystallization during the carburization process for its production, semi-finished product for gripping cabbage end parts
Case hardening steel with excellent prevention of the secondary recrystallization during the carburization process for its production, semi-finished product for gripping cabbage end parts
展开▼
机译:渗碳钢,具有出色的防渗碳过程中二次再结晶的能力,半成品可夹持白菜的端部零件
展开▼
页面导航
摘要
著录项
相似文献
摘要
A method of manufacturing case hardened steel, capable of minimizing stably the coarsening of particles therein in the carburizing and quenching step, comprising heating steel containing 0.015-0.04 % of Al, 0.005-0.04 % of Nb, 0.006-0.020 % of N and a specific range of percentage of other specific components at 1150 °C or above for 10 minutes or more, hot rolling the resultant steel at a finishing temperature of 920-1000 °C, and then gradually cooling the resultant product from 800 °C to 500 °C at a rate of 1 °C/sec or above: a case hardened steel manufactured by this method and having an amount of deposition of Nb (CN) after the hot rolling step of at least 0.005 %, an amount of deposition of AlN of at most 0.005 %, the number of Nb (CN) particles with diameters of at most 0.1 νm in a mother phase of the steel of at least 20/100 νm2, a content of a bainite structure of at most 30 % and a crystal grain number of ferrite of 8-11; and a raw shaped material for carburized parts made by utilizing the case hardened steel.
展开▼