FERRITIC STAINLESS STEEL WITH EXCELLENT HIGH-TEMPERATURE STRENGTH, HIGH-TEMPERATURE OXIDATION RESISTANCE AND HIGH-TEMPERATURE SALT DAMAGE RESISTANCE
FERRITIC STAINLESS STEEL WITH EXCELLENT HIGH-TEMPERATURE STRENGTH, HIGH-TEMPERATURE OXIDATION RESISTANCE AND HIGH-TEMPERATURE SALT DAMAGE RESISTANCE
展开▼
机译:具有出色的高温强度,高温抗氧化性和高温耐盐蚀性的铁素体不锈钢
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To produce ferritic stainless steel having excellent high-temperature strength, high-temperature oxidation resistance and high-temperature salt damage resistance and capable of withstanding use at high temperatures exceeding 900°C.;SOLUTION: Material components are regulated to a composition range consisting of, by mass, ≤0.02% C, 0.5 to 2.0% Si, ≤2.0% Mn, 12.0 to 16.0% Cr, 1.0 to 5.0% Mo, 2.0 to 5.0% W, 5(C+N) to 1.0% Nb, ≤0.02% N and the balance Fe with inevitable impurities.;COPYRIGHT: (C)2004,JPO