composition for reducing the eisenoxidbildung in slag from steel melts, and process for the production of a slag with low iron oxide content or
composition for reducing the eisenoxidbildung in slag from steel melts, and process for the production of a slag with low iron oxide content or
展开▼
机译:降低钢水熔渣中的艾森氧化能力的组合物,以及生产低氧化铁含量的渣的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
A composition comprising: from 50 to 60 wt-% of C, from 7 to 10 wt-% of Al, from 15 to 20 wt-% of Al2O3, from 7 to 10 wt-% of CaO and from 2 to 5 wt-% of MgO. A process for preparing such compsitions as well as a process for using such composition in the melting of scrap iron in a electric furnace with the aim of decreasing iron losses due to oxidation and of lowering iron oxide content of steel melting slag.
展开▼
机译:一种组合物,其包含:50-60重量%的C,7-10重量%的Al,15-20重量%的Al 2 O 3,7-10重量%的CaO和2-5重量%。 MgO%。制备这种组合物的方法以及在电炉中的废铁熔融中使用这种组合物的方法,目的是减少由于氧化引起的铁损失并降低钢熔渣的氧化铁含量。