Magnets of the ferrite type economic and pharmacological improved
Magnets of the ferrite type economic and pharmacological improved
展开▼
机译:经济和药理学上改进的铁氧体型磁铁
展开▼
页面导航
摘要
著录项
相似文献
摘要
Ferritic type magnets comprise a magnetoplumbite phase compound with a global performance index GIP of Br + 0.5 (Br is the remanent induction, as mT) and Hk of at least 580, preferably 585. Hk corresponds to the field H (kA.m) for B that is 0.9Br. Ferritic type magnets comprise a magnetoplumbite phase of formula (I). M1-xRxFe12-yTyO19 (I) M = Sr, Ba, Ca or Pb; R = rare earth metal or Bi; T = Co, Mn, Ni or Zn; x = 0.15-0.42; and alpha = y/x that is 0.5-0.9. The ferrite magnet has a reduced amount of element T and a global performance index GIP of Br + 0.5 (Br is the remanent induction, as mT) and Hk of at least 580, preferably 585. Hk corresponds to the field H (kA.m) for B that is 0.9Br. Independent claims are included for the preparation and use of the magnets.
展开▼
机译:铁氧体型磁体包含磁铅石相化合物,其整体性能指数GIP为Br + 0.5(Br为剩磁,以mT计)且Hk至少为580,最好为585。Hk对应于磁场H(kA.m) B为0.9Br。铁氧体型磁体包括式(I)的磁铅矿相。 M1-xRxFe12-yTyO19(I)M = Sr,Ba,Ca或Pb; R =稀土金属或Bi; T = Co,Mn,Ni或Zn; x = 0.15-0.42;和alpha = y / x,为0.5-0.9。铁氧体磁体的元素T量减少,并且总性能指数GIP为Br + 0.5(Br为剩磁,以mT计)且Hk至少为580,最好为585。Hk对应于磁场H(kA.m ),即B为0.9Br。磁铁的制备和使用包括独立权利要求。
展开▼