ELECTROCRYSTALLIZATION PLATING BATH FOR FORMING MAGNETIC FILM, AND ELECTROCRYSTALLIZATION PLATING METHOD USING THE SAME
ELECTROCRYSTALLIZATION PLATING BATH FOR FORMING MAGNETIC FILM, AND ELECTROCRYSTALLIZATION PLATING METHOD USING THE SAME
展开▼
机译:用于形成磁性膜的电结晶镀浴以及使用该方法的电结晶镀方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide an electrocrystallization plating liquid for forming an Fe-Pt alloy magnetic film and an Fe-Pd alloy magnetic film as a new electrocrystallization plating bath for diversifying the magnetic film composing a magnetic recording medium and forming the magnetic film at a large scale and low cost.;SOLUTION: The electrocrystallization plating bath for forming a magnetic film of an iron-platinum alloy comprises: 1 to 50 g/L iron sulfate heptahydrate; 2 to 60 g/L chloroplatinic acid (IV); 0.5 to 50 g/L ammonium tartrate; and 5 to 250 g/L ammonia. The electrocrystallization plating bath for forming a magnetic film of an iron-palladium alloy comprises: 1 to 50 g/L iron sulfate heptahydrate; 0.2 to 50 g/L palladium chloride; 0.5 to 70 g/L ammonium tartrate; 0.5 to 30 g/L ammonium chloride; and 0.1 to 10 g/L cresolsulfonic acid.;COPYRIGHT: (C)2005,JPO&NCIPI
展开▼
机译:解决的问题:提供一种用于形成Fe-Pt合金磁性膜的电结晶镀液和一种Fe-Pd合金磁性膜的新型电结晶镀浴,以使构成磁记录介质的磁性膜多样化并在其上形成磁性膜。解决方案:用于形成铁-铂合金磁性膜的电结晶镀浴包括:1至50 g / L七水合硫酸铁; 2至60 g / L氯铂酸(IV); 0.5至50 g / L酒石酸铵;和5至250 g / L的氨水。用于形成铁-钯合金的磁性膜的电结晶镀浴包括:1至50g / L的七水合硫酸铁;和0.2至50 g / L氯化钯; 0.5至70 g / L酒石酸铵; 0.5至30 g / L氯化铵;和0.1至10 g / L的甲酚磺酸。;版权:(C)2005,JPO&NCIPI
展开▼