REFRACTORY, CHROME-ALUMINA-BASED MATERIAL, CHROME-ALUMINA BRICK AND USE OF THE BRICK
REFRACTORY, CHROME-ALUMINA-BASED MATERIAL, CHROME-ALUMINA BRICK AND USE OF THE BRICK
展开▼
机译:铬铝基耐火材料,铬铝砖及砖的使用
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to a chromium-corundum-based refractory material comprising: -5 to 35% by weight, preferably 10 to 30% by weight, of a Cr2O3 component having a particle size of less than 0.1 mm, -1 to 10% by weight, preferably 3 - between 55 and 94% by weight, preferably between 62 and 87% by weight, of an alumina (corundum) component with a particle size of between 0,2 and 4%, It is between 0 mm.
展开▼
机译:铬刚玉基耐火材料技术领域本发明涉及一种铬刚玉基耐火材料,其包含:-5至35重量%,优选10至30重量%的Cr 2 O 3成分,其粒径小于0.1mm,-1至10%。重量比,优选3-55-94重量%,优选62-87重量%的氧化铝(刚玉)组分,其粒度为0.2-4%,其为0mm。