Lead-free and preferably arsenic-free lanthanum heavy flint glassesAbstractThe invention relates to lead-free and preferably arsenic-free optical glasses having a refractive index n[err] of 1.84 [err] n[err] [err] 1.96 and an Abb[err] number v[err] of 27 [err] v[err] [err] 36, with good chemical resistance, excellent crystallization resistance and the following composition (in % by weight based on oxide):[err] In addition, the glass according to the invention, as well as having a maximum alkali metal oxide content of 10% y weight, may also contain standard refining agents, although arsenic is not preferred.The present invention also relates to the use of the glass according to the invention in the application areas of imaging) projection, telecommunications, optical communication technology and/or laser technology.
展开▼
机译:无铅,最好无砷的镧重火石玻璃抽象本发明涉及具有1.84 [err] n [err] [err] 1.96的折射率n [err]和27 [err]的阿贝[err]值v [err]的无铅且优选无砷的光学玻璃。 ] v [err] [err] 36,具有良好的耐化学性,优异的抗结晶性和以下组成(以氧化物计,以重量%计):[呃] 另外,根据本发明的玻璃,以及最大碱金属氧化物含量为10重量%,也可以包含标准的澄清剂,尽管砷不是优选的。本发明还涉及根据本发明的玻璃在成像投影,电信,光通信技术和/或激光技术的应用领域中的用途。
展开▼