METHOD FOR ACCELERATED TEST OF ALUMINIDE COATING FOR HIGH- TEMPERATURE CORROSIVE DURABILITY
METHOD FOR ACCELERATED TEST OF ALUMINIDE COATING FOR HIGH- TEMPERATURE CORROSIVE DURABILITY
展开▼
机译:高温腐蚀耐久性的铝化物涂层加速试验方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
FIELD: corrosion resistance tests, in particular method for accelerated test of aluminide coating for high-temperature corrosive durability.;SUBSTANCE: claimed method includes sample salt corrosion test at 9000C. Sample is placed over crucible containing (mass %): sodium sulfate 48; sodium chloride 17; magnesium sulfate 15; iron(III) chloride; vanadium(V) oxide; calcium chloride 5. Corrosion durability is defined as augmentation of weight increment more than 10 g/m2for 3 h. Method of present invention may be used to select coat with the most endurance.;EFFECT: decreased test time and natural-like test condition.
展开▼
机译:领域:耐腐蚀性测试,特别是用于加速铝化物涂层高温腐蚀性的加速测试的方法。依据:所要求保护的方法包括在900 0 Sup> C下进行样品盐腐蚀测试。将样品置于含有(质量%):硫酸钠48的坩埚上。氯化钠17;硫酸镁15;氯化铁(III);氧化钒(V);氯化钙5.腐蚀耐久性定义为重量增加超过10 g / m 2 Sup> 3小时。本发明的方法可以用于选择具有最大耐久性的涂层。效果:减少了测试时间和类似自然的测试条件。
展开▼