HIGH-TEMPERATURE NICKEL-BASED WELDABLE ALLOY AND ARTICLE MADE FROM THIS ALLOY
HIGH-TEMPERATURE NICKEL-BASED WELDABLE ALLOY AND ARTICLE MADE FROM THIS ALLOY
展开▼
机译:高温镍基可焊合金及由该合金制成的制品
展开▼
页面导航
摘要
著录项
相似文献
摘要
FIELD: metallurgy; high-temperature nickel-based weldable alloys for manufacture of housings, casings, heat shields and other units working at temperature of up to 900ºC.;SUBSTANCE: proposed alloy contains carbon, chromium, molybdenum, niobium, aluminum, titanium, zirconium, boron and magnesium, cobalt, tungsten and lanthanum at the following content of components, mass-%: carbon, 0.02-0.10; chromium, 12.0-20.0; cobalt, 8.0-20.0; molybdenum, 3.5-7.0; tungsten, 0.5-3.0; niobium, 3.2-6.5; aluminum, 1.0-1.8; titanium, 1.0-1.6; zirconium, 0.4-1.4; boron, 0.0001-0.006; magnesium, 0.003-0.06; lanthanum, 0.0030-0.08; the remainder being nickel.;EFFECT: improved strength characteristics within range of working temperatures; enhanced plasticity; avoidance of drop in plasticity; satisfactory weldability and heat resistance.;3 cl, 2 tbl, 1 ex
展开▼
机译:领域:冶金;高温镍基可焊接合金,用于制造外壳,壳体,隔热罩和其他在最高900°C的温度下工作的部件。物质:建议的合金包含碳,铬,钼,铌,铝,钛,锆,硼和镁,钴,钨和镧的以下成分含量(质量%):碳0.02-0.10;铬12.0-20.0;钴8.0-20.0;钼3.5-7.0;钨0.5-3.0;铌3.2-6.5;铝1.0-1.8;钛1.0-1.6;锆0.4-1.4;硼,0.0001-0.006;镁0.003-0.06;镧0.0030-0.08;效果:在工作温度范围内改善了强度特性;增强的可塑性;避免可塑性下降;令人满意的可焊性和耐热性。; 3 cl,2 tbl,1 ex
展开▼