EPOXY RESIN COMPOSITION, FIRER-REINFORCED COMPOSITE MATERIAL, AND METHOD FOR PRODUCING FIRER-REINFORCED COMPOSITE MATERIAL
EPOXY RESIN COMPOSITION, FIRER-REINFORCED COMPOSITE MATERIAL, AND METHOD FOR PRODUCING FIRER-REINFORCED COMPOSITE MATERIAL
展开▼
机译:环氧树脂组合物,弗瑞尔增强复合材料以及生产弗瑞尔增强复合材料的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide an epoxy resin composition which has excellent productivity and heat resistance, to provide a firer-reinforced composite material, and to provide a method for producing the same.;SOLUTION: This epoxy resin composition is characterized by satisfying the following expressions (1) to (4) at a curing temperature Tc included in a range of 60 to 180°C. (1) 1≤t10≤10, (2) 3≤t90≤30, (3) 1≤t90/t10≤3, (4) Tg≥Tc+20, wherein t10 : a time (minute) from a measurement-starting time to a time reaching a cure index of 10%, on a dielectric measurement at a curing temperature Tc; t90: a time (minute) from a measurement-starting time to a time reaching a cure index of 90%, on a dielectric measurement at a curing temperature Tc; Tg: the glass transition temperature (°C) of an epoxy resin composition at the passage point of t90 (minute).;COPYRIGHT: (C)2006,JPO&NCIPI
展开▼
机译:解决的问题:提供一种具有优异的生产率和耐热性的环氧树脂组合物,提供一种耐火剂增强的复合材料,以及提供一种其制备方法。在包括在60至180℃范围内的固化温度Tc下,满足以下表达式(1)至(4)。 (1)1≤ t 10 Sub>≤ 10,(2)3≤ t 90 Sub>≤ 30,(3)1≤ t 90 Sub> / t 10 Sub>≤ 3,(4)Tg≥ Tc + 20,其中t 10 Sub>:从测量开始时间到达到测量时间的时间(分钟)在固化温度Tc下进行介电测量时,固化指数为10%; t 90 Sub>:在固化温度Tc下进行电介质测量时,从测量开始时间到达到固化指数90%的时间(分钟); Tg:在t 90 Sub>的通过点处环氧树脂组合物的玻璃化转变温度(℃)(分钟)。;版权:(C)2006,JPO&NCIPI
展开▼